Heat transfer at the metal/chill interface during solidification of commercially pure aluminium square bar castings with cast iron chill at one end was investigated. Experiments were carried out for different chill thicknesses and superheats. The inner surface temperature of the chill initially was found to increase at a faster rate for higher superheats. The effect of chill thickness on the inner surface temperature of the chill was observed only after the heat from the solidifying casting had sufficient time to diffuse to the interior of the chill material. Inverse analysis of the non-linear one-dimensional Fourier heat conduction equation indicated the occurrence of peak heat flux at the end of filling of the mould. The effect of superheat on heat flux was minimal after filling. However, the effect of chill thickness had a significant effect on the heat flux after the occurrence of peak heat flux. Higher heat flux transients were estimated for …