Titanium oxides were reduced to metallic titanium using the liquid calcium floating on the molten CaCl₂. A part of Ca dissolved into CaCl₂ and reacted with TiO₂ settled below CaCl₂. The by-product CaO also dissolved by about 20 mol pct into CaCl₂, which was effective in reducing the oxygen concentration in the obtained Ti particles. The compositional region in the Ca-CaCl₂-CaO system was examined for the less oxygen contamination in Ti and the better handling in leaching. A large amount of the residual calcium oxidized the titanium powder in leaching. The metallic Ti powder less than 1000 mass ppm oxygen could be obtained only for 3.6 ks using 5 to 7 mol pct Ca-CaCl₂ at 1173 K. The powder was slightly sintered like sponge, and contained approximately 1500 ppm Ca. The anatase phae, the intermediate product in the refining process of TiO₂, could be also supplied as raw material as well as rutile.