Ceramic membranes (CMs) with different pore sizes (0.14 μm CM1, 150 kDa CM2 and 5 kDa CM3) were tested as separators in two-chamber microbial fuel cells (MFCs). The performance and ionic gradient concentration of MFCs using CMs were compared with that of cation exchange membrane (CEM), Nafion 117. MFC with CMs exhibited a higher performance than that of CEM under batch operation. The highest power density of 1790 ± 60 mW/m², columbic efficiency (CE) of 41 ± 10% and internal resistance of 102 ± 13 Ω were obtained for MFC with CM3 under batch mode operation. The highest power density, columbic efficiency and internal resistance of MFC with CEM were found to be 1225 ± 20 mW/m², 21 ± 1% and 400 ± 10 Ω, respectively. The highest performance of MFC with CM3 was expected due to a higher porosity of CM3 (13.8%) compared with that of CM1 (11.0%) and CM2 (11.05%). MFCs …