Starch-based biomaterials and scaffolds have been proposed for several biomedical applications. In the present work new scaffolds based on a 50/50 (wt%) blend of corn starch/ethylene-vinyl alcohol (SEVA-C) were studied. These scaffolds were processed by a melt-based technology, which has been used before with other starch-based materials but never with SEVA-C. Scanning electron microscopy (SEM) observation showed that the developed porous structures were 60% porous with pore size between 200 and 900 μm and a reasonable degree of interconnectivity. Moreover, scaffolds presented a compressive modulus of 117.50 ± 3.7 MPa and a compressive strength of 20.8 ± 2.4 MPa. Cytotoxicity evaluation was performed according to ISO/EN 10993 part 5 guidelines, and revealed that the developed scaffolds were nontoxic and did not inhibit cell growth. Direct contact assays were also …