In the present paper the effect of the presence of Na₂CO₃ on the etching characteristics of NaOH has been presented quantitatively. Six CR-39 detectors were etched at 50, 60 and 70^∘C in 6M NaOH solutions containing 0%, 1%, 2%, 3%, 4% and 5% concentration of Na₂CO₃. Etching was performed in 22 steps of 5–10min starting from 15min up to 210min. These detectors were previously exposed to ²⁵²Cf source. Lengths of 35 randomly selected fission fragment tracks were measured after each etching time interval. Similarly, diameters of 25 randomly selected fission fragments having 90^∘ incidence angle were also measured as mentioned above. Track etch rate, bulk etch rate, etching efficiency and activation energies of both track as well as bulk etching have been determined.