查看文章

Three‐dimensional macroporous titanium–aluminum–vanadium (TiAl6V4) implants produced by additive manufacturing (AM) can be grit blasted (GB) to yield microtextured exterior surfaces, with additional micro/nano‐scale surface features provided by subsequent acid etching (AE). However, the line‐of‐sight nature of GB causes the topography of exterior GB + AE‐modified surfaces to differ from internal GB‐inaccessible surfaces. Previous in vitro studies using dense TiAl6V4 substrates indicated that a nonline‐of‐sight, calciothermic‐reaction (CaR)‐based process provided homogeneous osteogenic nanotextures on GB + AE surfaces, suggesting it could be used to achieve a homogeneous nanotopography on external and internal surfaces of macroporous AM constructs. Macroporous TiAl6V4 (3D) constructs were produced by direct laser melting and modified by GB + AE, with the CaR process then …