The atom transfer radical polymerization (ATRP) of styrene and acrylates from silicon wafers modified with an initiator layer composed of 2-bromoisobutyrate fragments is described. In the presence of the proper ratio of activating and deactivating transition-metal species, controlled radical polymerizations of styrene were observed such that the thickness of the layer consisting of chains grown from the surface increased linearly with the molecular weight of chains polymerized in solution in identical, yet separate, experiments. The layer thickness increased linearly with reaction time for ATRP of styrene and methyl acrylate due to both the extremely low initiator concentration relative to monomer and the low monomer conversion. Further evidence for control was observed by the polymerization of blocks of either methyl or tert-butyl acrylate from the polystyrene layer. Modification of the hydrophilicity of the surface layer …