查看文章

Nickel-chromium alloys have been used as coatings to deal with oxidation environments at high temperature. The present work is a comparative study of HVOF and cold sprayed Ni-20Cr coating on a boiler steel (SAE 213-T22) in a molten salt environment of Na 2 SO 4-60% V 2 O 5 at 900 C under cyclic conditions. The weight change technique was used to establish the kinetics of corrosion. X-ray diffraction, surface and cross-sectional FE-SEM/EDS techniques were used to analyse the corrosion products. The hot corrosion resistance of both the coatings was better than the uncoated steel. This may be attributed to the formation of oxides and spinels of nickel and chromium in the coated steels. These oxides might have blocked the pores and splat boundaries, and acted as diffusion barriers to the inward diffusion of corroding species. Based upon the overall results and subsequent analysis of hot-corrosion data the …