Nickle zinc ferrite (NiZnFe₂O₄) magnetic nanoparticle (MNPs) has been successfully synthesized using co-precipitation method. NiZnFe₂O₄ was coated SiO₂ (NiZnFe₂O₄/SiO₂) using Stöber method with various concentrations of (5%, 10%, 15%, 20%, 30%, and 50%). MNPs sample has a spinel ferrite phase confirmed by X-ray diffraction (XRD) measurements. The results of the functional group analysis performed using Fourier transform infrared (FTIR) showed an M-O tetrahedral vibrational bond found a wavelength of 347 cm^-1. After coated silica, Si-O-Si vibrational bonds appear at wavelengths of 1033.85 cm¹. Magnetic properties were measured using vibrating Sample Magnetometer (VSM), the result shows that has maximum saturation magnetization of NiZnFe₂O₄ 22.5 emu.gram^-1 and decreased to 16.9 emu.gram^-1 after coating. In figure 1 show that the photodegradation activity of MNPs was carried out …