This study investigates the preparation of polyetherimide (PEI) – LaNi₅ composites films for hydrogen storage. Prior to the polymer addition, LaNi₅ was ball-milled at different conditions (250, 350, and 450 RPM) and annealed at 500 °C for 1 h under vacuum. The composites were produced with BM-LaNi₅-350 (PEI/LaNi₅-350) and annealed BM-LaNi₅-350 (PEI/LaNi₅-350-TT). Membranes were successfully produced through solvent casting assisted by an ultrasonic bath. The particles dispersion and the film morphology did not change after hydrogenation cycles. In the H₂ sorption experiments at 43 °C and 20 bar, the films stored H₂ without incubation time; both samples reached a capacity of ~0.6 wt%. The H₂ sorption kinetics of PEI/LaNi₅-350 was comparable to that of BM-LaNi₅-350, whereas PEI/LaNi₅-350-TT presented significantly slower kinetics. LaNi₅ oxidation was hindered by PEI, showing that it can be …