Exfoliated nanocomposites of polyamide 6 (PA6) with residual monomer and an organically treated montmorillonite (3 and 5 wt %) were produced by twin‐screw extrusion. The composites had their steady state, dynamic, and transient rheological properties measured by parallel‐plates rheometry; their exfoliation level was characterized by wide angle X‐rays diffraction (WAXD) and transmission electron microscopy (TEM). The characterization showed as follows: (i) the nanoclay's lamellas were well dispersed and distributed thru the PA6, (ii) the postpolymerization of the residual monomer produced more branched chains than linear ones in the pure PA6, (iii) the nanoclay's lamellas acted as entanglement points in the nanocomposites, and (iv) the molecular weight of the PA6 in the nanocomposites decreased. Blown films of the nanocomposites were produced by single screw extrusion; the die pressure during the …