In this work, we reported the synthesis of monophasic boron-containing mullite (MBM) fibers
using basic aluminum acetate (BAA) and tetraethyl orthosilicate (TEOS) as starting materials …

Mullite fibres with uniform diameter and smooth surface have been synthesized using
commercial grade polyvinyl butyral (PVB) as binder. The sol with good spinnablity was …

In the present work, continuous mullite fibers were fabricated through the diphasic sol-gel
route using aluminum isopropoxide (AIP) and aluminum nitrate (AN) as the alumina sources …

Rich silica mullite fibers were prepared from an aqueous solution of aluminum lactate and
silica sol by the sol–gel method, in which the Al/Si molar ratio of fibers was 0.64. The …

Continuous mullite ceramic fibers were fabricated by a sol–gel dry spinning process and
sintered at 1100° C to examine the influence of the solid content and process parameters on …

Long mullite fibers were prepared by a sol-gel method using aluminum nitrate, tartaric acid
and tetraethylorthosilicate (TEOS). Thermogravimetry-differential scanning calorimetry (TG …

Polycrystalline mullite fibers and novel zirconia-toughened mullite (ZTM) fibers with average
diameters between 9.7 and 10.3 μm containing 3, 7 and 15 wt.-% tetragonal ZrO 2 (ZTM3 …

Continuous mullite fibers with ultrafine diameters and good thermal stability are an ideal
candidate to be used to prepare ceramic-based aerogels, sponges, or composites. In the …

The effect of thermal exposure on a mullite fiber was analyzed. This type of mullite fiber,
consisting of γ-Al 2 O 3 and amorphous SiO 2, was developed for high-temperature …

Highly porous mullite fiber-based ceramics with a three-dimensional cross structure were
successfully designed and fabricated by filtration method. To address the thermal migration …