In the field of orthopedics, magnesium (Mg) and magnesium-based composites as biodegradable materials have attracted fundamental research. However, the medical applications of magnesium implants have been restricted owing to their poor corrosion resistance, especially in the physiological environment. To improve the corrosion resistance of Mg/HA/TiO₂ nanocomposites, monolayer MgO and double-layer Si/MgO coatings were fabricated layer-by-layer on the surface of a nanocomposite using a powder metallurgy route. Then, coating thickness, surface morphology, and chemical composition were determined, and the corrosion behavior of the uncoated and coated samples was evaluated. Field-emission scanning electron microscopy (FE-SEM) micrographs show that an inner MgO layer with a porous microstructure and thickness of around 34 μm is generated on the Mg/HA/TiO₂ nanocomposite substrate, and that the outer Si layer thickness is obtained at around 23 μm for the double-layered coated sample. Electrochemical corrosion tests and immersion corrosion tests were carried out on the uncoated and coated samples and the Si/MgO-coated nanocomposite showed significantly improved corrosion resistance compared with uncoated Mg/HA/TiO₂ in simulated body fluid (SBF). Corrosion products comprising Mg(OH)₂, HA, Ca₃(PO₄)₂, and amorphous CaP components were precipitated on the immersed samples. Improved cytocompatibility was observed with coating as the cell viability ranged from 73% in uncoated to 88% for Si/MgO-coated Mg/HA/TiO₂ nanocomposite after nine days of incubation.