Preparation and characterization of Cu and Zn modified nickel manganite NTC powders and thick film thermistors
OS Aleksic, MV Nikolic, MD Lukovic, N Nikolic… - Materials Science and …, 2013 - Elsevier
A simple ball milling/thermal treatment procedure was applied to obtain fine thermistor
powders. Three different powder compositions were analyzed–Cu0. 2Ni0. 5Zn1. 0Mn1. 3O4,
Cu0. 25Ni0. 5Zn1. 0Mn1. 25O4 and Cu0. 4Ni0. 5Mn2. 1O4. XRD analysis showed that all
three powder compositions had a cubic spinel structure. Correlation between the sintering
temperature, structure and resulting electrical properties was analyzed on bulk samples.
Thick film pastes were composed and segmented thick film thermistors were screen printed …
powders. Three different powder compositions were analyzed–Cu0. 2Ni0. 5Zn1. 0Mn1. 3O4,
Cu0. 25Ni0. 5Zn1. 0Mn1. 25O4 and Cu0. 4Ni0. 5Mn2. 1O4. XRD analysis showed that all
three powder compositions had a cubic spinel structure. Correlation between the sintering
temperature, structure and resulting electrical properties was analyzed on bulk samples.
Thick film pastes were composed and segmented thick film thermistors were screen printed …