Hydrothermal preparation of calcium hydroxyapatite powders
T Hattori, Y Lwadate - Journal of the American ceramic Society, 1990 - Wiley Online Library
Calcium hydroxyapatite powders were prepared by hydrothermal reactions of calcium
pyrophosphate and calcium oxide. Primary particles of the hydroxyapatite obtained were …
pyrophosphate and calcium oxide. Primary particles of the hydroxyapatite obtained were …
[引用][C] Hydrothermal synthesis of hydroxyapatite from calcium pyrophosphate
T Hattori, Y Iwadate, T Kato - Journal of materials science letters, 1989 - Springer
Hydroxyapatite as well as tricalcium phosphate is known to be biocompatible with human
bone and tooth. Advances in biomaterials are occurring at an accelerated rate and much …
bone and tooth. Advances in biomaterials are occurring at an accelerated rate and much …
Calcium apatite prepared from calcium hydroxide and orthophosphoric acid
A Osaka, Y Miura, K Takeuchi, M Asada… - Journal of Materials …, 1991 - Springer
Calcium hydroxyapatite has been prepared due to a direct precipitation reaction between
0.3 m orthophosphoric acid solution and 0.1 mol calcium hydroxide dispersed in 200 ml …
0.3 m orthophosphoric acid solution and 0.1 mol calcium hydroxide dispersed in 200 ml …
Carbonate-doped hydroxyapatite
EG Nordström, KH Karlsson - Journal of Materials Science: Materials in …, 1990 - Springer
A hydroxyapatite slurry was prepared by stirring into water a stoichiometric mixture of
tricalcium phosphate and calcium hydroxide until the solid content was 50 wt%. Samples …
tricalcium phosphate and calcium hydroxide until the solid content was 50 wt%. Samples …
Hydrothermal synthesis of various carbonate containing calcium hydroxyapatites
DM Roy, W Eysel, D Dinger - Materials Research Bulletin, 1974 - Elsevier
Carbonate containing hydroxyapatites were prepared hydrothermally between 2000 and
20,000 psi and 250 and 900° C using H 2 O or CO 2 pressure. On the basis of IR, x-ray and …
20,000 psi and 250 and 900° C using H 2 O or CO 2 pressure. On the basis of IR, x-ray and …
Hydroxyapatite synthesized by a simplified hydrothermal method
HS Liu, TS Chin, LS Lai, SY Chiu, KH Chung… - Ceramics …, 1997 - Elsevier
A simplified hydrothermal method of synthesizing hydroxyapatite powder is described.
Heating powders of Ca (OH) 2, Ca (H2PO4) 2· H2O and distilled water in a pressurized pot …
Heating powders of Ca (OH) 2, Ca (H2PO4) 2· H2O and distilled water in a pressurized pot …
A new synthesis of hydroxyapatite
W Weng, JL Baptista - Journal of the European Ceramic Society, 1997 - Elsevier
An ethylene glycol solution of Ca (OAC) 2. xH2O and a butanol solution of P2O5 were used
as precursors to produce hydroxyapatite. Acetic acid (HOAC) and ammonium nitrate …
as precursors to produce hydroxyapatite. Acetic acid (HOAC) and ammonium nitrate …
New processing technique for hydroxyapatite ceramics by the hydrothermal hot‐pressing method
K Hosoi, T Hashida, H Takahashi… - Journal of the …, 1996 - Wiley Online Library
A new processing technique for preparing hyroxyapatite (HAp) ceramics has been
developed using the hydrothermal hot‐pressing (HHP) method. Powder mixed dibasic …
developed using the hydrothermal hot‐pressing (HHP) method. Powder mixed dibasic …
Low temperature sintering of hydroxyapatite by hydrothermal hot-pressing
K IOKU, K YAMAMOTO, K YANAGISAWA… - Phosphorus Research …, 1994 - jstage.jst.go.jp
The powder of amorphous calcium phosphate(ACP) containing 20mass% water, prepared
from aqueous solution of Ca (NO3) 2 and(NH4) 2HPO4, was hot-pressed hydrothermally at …
from aqueous solution of Ca (NO3) 2 and(NH4) 2HPO4, was hot-pressed hydrothermally at …
Hydrothermal synthesis of hydroxyapatite from octacalcium phosphate: effect of hydrothermal temperature
M Kamitakahara, N Ito, S Murakami… - Journal of the Ceramic …, 2009 - jstage.jst.go.jp
Hydroxyapatite (HA) was synthesized by the hydrothermal treatment of octacalcium
phosphate (OCP). Powder of OCP was hydrothermally treated with distilled water at 120 …
phosphate (OCP). Powder of OCP was hydrothermally treated with distilled water at 120 …