Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan, J Hu… - Acta Materialia, 2021 - Elsevier
Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …
被引用次数：27 相关文章

Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li - Acta Materialia, 2021 - inis.iaea.org
[en] Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …

Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan… - Acta …, 2021 - ui.adsabs.harvard.edu
Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …

Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

PH Cao, KP So, Y Yang, JG Park, MD Li… - ACTA …, 2021 - scholarworks.bwise.kr
Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …
[PDF] mit.edu

[PDF][PDF] Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan, J Hu… - Acta Materialia, 2021 - li.mit.edu
abstract Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …
[PDF] 18.18.54.15

[PDF][PDF] Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan, J Hu… - Acta Materialia, 2021 - 18.18.54.15
abstract Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …

Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan, J Hu… - Acta Materialia, 2020 - osti.gov
Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other radiation defect sinks are …

Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan, J Hu… - 2021 - dspace.mit.edu
© 2020 Acta Materialia Inc. Radiation damage of structural materials leads to mechanical
property degradation, eventually inducing failure. Secondary-phase dispersoids or other …

Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan, J Hu… - Acta …, 2021 - pure.psu.edu
Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …
[PDF] mit.edu

[PDF][PDF] Carbon nanotube (CNT) metal composites exhibit greatly reduced radiation damage

P Cao, KP So, Y Yang, JG Park, M Li, L Yan, J Hu… - Acta Materialia, 2021 - li.mit.edu
abstract Radiation damage of structural materials leads to mechanical property degradation,
eventually inducing failure. Secondary-phase dispersoids or other defect sinks are often …