Y(Ba_1-xK_x)₂Cu₃O_7-δ ceramics (x = 0.00, 0.03, 0.05 and 0.08) were synthesized by thermal treatments of aqueous solution of metals nitrates and polyvinyl pyrrolidone (PVP) that acts as a capping agent. The effects of K-substitution on the crystal structure, microstructure and electrical resistance of samples were investigated. The X-ray diffractions results indicated an improvement of crystallinity and variation of lattice constant, a, b and c of YBa₂Cu₃O_7-δ (Y123) phase with K-substitution. The K-substitution resulted in increasing of orthorhombicity factor compared to pure Y123. Microstructural observation using scanning electron microscopy showed that K-substitution promotes the grain growth of Y123. The superconducting transitions (T_c) of the substituted-samples were higher than that of the pure Y123. The T_c (onset) were 93, 97, 95, 95 K for the samples with x = 0.00, 0.03, 0.05 and 0.08, respectively. Comparing with pure sample, the substituted-samples showed sharper superconducting transition (ΔT_c). The best superconducting properties was observed for sample with x = 0.03.