Abstract Preparation of 3-mercaptopropyl) trimethoxylsilane (PropS-SH) film on brass
surface and its corrosion resistance performance were investigated by surface energy …

The corrosion product formation and the stress corrosion cracking of brass in different
ammonia environments have been observed and characterized. Optical and scanning …

This study investigated the micro and nanoscale structure in Cu-Zn alloy, as well as its
corrosion patterns. To achieve this goal, a set of Roman orichalcum coins were analysed …

The influence of the grain tolerance angle (GTA) on the microstructural parameters of
pearlitic steel is investigated using electron backscattered diffraction. The corrosion behavior …

The fracture behavior of an electro-connector brass bolt with the strength of 360 MPa was
experimentally studied by means of visual inspection, macroscopic and microscopic …

Abstract HAl77-2 aluminum brass (UNS C68700) tubes with equiaxed grain (EG) structure
and with an axial-oriented columnar grain (CG) structure were prepared by the traditional …

This study evaluates the nucleation criterion for intergranular stress corrosion cracking
(SCC) on a smooth surface of type 304 austenitic stainless steel from a mechanical …

Failure assessment was carried out on admiralty brass tubes in a heat exchanger that failed
after five years of service. The failed tubes had numerous circumferential grooves on the …

We use the magnetron sputtering method to fabricate FePt thin films on amorphous oxidized
Si substrates by controlling the sputtering pressure and investigate the evolution of …

Abstract Orichalcum is a Cu-Zn based alloy known since the 1st millennium BC. The
cementation was the ancient technique used for its production. The PhD project here …