Bonding performance evaluation between the new nano-hydroxyapatite composite resin and dentin
Z Meng-meng, W Qing-shan, W Shuang… - Shanghai Journal of …, 2013 - sjos.cn
PURPOSE: To evaluate the shear bond strength and bonding ability between the new nano-
hydroxyapatite composite resin and tooth structure. METHODS: Thirty-six healthy isolated …
hydroxyapatite composite resin and tooth structure. METHODS: Thirty-six healthy isolated …
新型纳米羟基磷灰石复合树脂与牙本质的黏结性能评价
赵蒙蒙， 王青山， 王爽， 王方辉， 舒静媛 - 上海口腔医学, 2013 - sjos.cn
目的: 检测新型纳米羟基磷灰石复合树脂与牙本质间的黏结强度, 评价该材料对牙体组织的黏结
性能. 方法: 健康离体磨牙36 颗, 随机分为3 组, 制作牙本质黏结面, 分别黏结纳米羟基磷灰石 …
性能. 方法: 健康离体磨牙36 颗, 随机分为3 组, 制作牙本质黏结面, 分别黏结纳米羟基磷灰石 …
[PDF][PDF] Study on Preparation and Characterization of β-Cyclodextrin/Hydroxyapatite
Z Cui, A Zhou - 2016 - pdf.hanspub.org
Study on Preparation and Characterization of β-Cyclodextrin/Hydroxyapatite β-环糊精/羟基
磷灰石的制备与性能研究 Page 1 Hans Journal of Chemical Engineering and Technology …
磷灰石的制备与性能研究 Page 1 Hans Journal of Chemical Engineering and Technology …
β-环糊精/羟基磷灰石的制备与性能研究
崔真真， 周奥佳 - Hans Journal of Chemical Engineering and …, 2016 - hanspub.org
本研究分别以CaCl 2 和H 3 PO 4 为钙源和磷源, NaOH 为pH 调节剂, 成功制备了β-环糊精(β-
CD)/羟基磷灰石(HAP) 复合物. 借助傅里叶变换红外光谱(FT-IR), 热重分析(TG) …
CD)/羟基磷灰石(HAP) 复合物. 借助傅里叶变换红外光谱(FT-IR), 热重分析(TG) …
涤纶过滤布表面热压法固着羟基磷灰石颗粒
蒋臻， 王晓， 吕丽华， 崔永珠， 马春 - 大连工业大学学报, 2015 - cqvip.com
通过热压法在涤纶过滤布表面固着羟基磷灰石颗粒, 探讨了热压工艺对颗粒固载率和孔径的影响
. FT-IR 结果表明, 562,601 和1026cm-1 处出现振动吸收峰; XRD 结果表明, 在25.45°, 31.78° …
. FT-IR 结果表明, 562,601 和1026cm-1 处出现振动吸收峰; XRD 结果表明, 在25.45°, 31.78° …