Q345 steel was coated by hot dipping into molten pure aluminum and Al-Si baths. The
coatings were annealed at 800 and 900° C for 1–3 h and subsequently oxidized at 900° C …

This paper studied isothermal and thermocyclic boroaluminizing in pastes on low carbon
steels (0.2 wt.% carbon) through Thermodynamic evaluation of potential reactions in Boron …

Low carbon steel was plasma pack aluminized at 973 K (700° C) for 5, 10, and 15 minutes in
vacuum of 15 mbar. A paste of aluminum was packed around the samples, and the process …

High temperature oxidation of low carbon steel (SAPH440) with and without a hot-dip Al
coating in an atmosphere containing burning ethanol, water vapor, and air were studied by …

The AISI 1020 steel was coated by dipping it into the molten Al bath at 700 C for 16s. The
coating layer formed on the steel substrate is consisting of Al with a little Fe, FeAl 3 and Fe 2 …

Q345 steel is widely used in the construction industry, vehicle manufacturing industry, bridge
construction industry and many other aspects due to its excellent comprehensive …

Q345 steel was coated by hot dipping into molten pure aluminum and Al-Si baths. The
coatings were annealed at 800 and 900◦ C for 1–3 h and subsequently oxidized at 900◦ C …

The oxidation behavior of hot-dip aluminized AISI 1020 steel was studied at temperatures
700, 750, and 800° C in air and water-vapor at atmospheric pressure. The high temperature …

В работе проведено исследование изотермического и термоциклического
бороалитирования стали 20, установлен интервал температур термоциклирования …

AISI 1020 steel was coated by dipping into a molten Al bath at 700° C for 16s. The coating
layer formed on the steel substrate is consisting of Al with a little Fe, FeAl3 and Fe2Al5 …