This review focuses on the effect of initial corrosion of hot-dip galvanized reinforcement in
both fresh and curing concrete on total bond strength. Corrosion behavior of hot-dip …

Corrosion of reinforcement is one of the leading causes of the deterioration in reinforced
concrete structures. RC structures damaged by reinforcement corrosion can exhibit not only …

The problem of the durability of reinforced concrete structures is arisen, dramatically, in the
last decades, showing that one of the most dangerous degradation phenomena is …

The reinforced concrete (RC) columns infiltrated by chloride ion in marine environment are
much vulnerable under seismic loading. In this paper, the hysteretic behaviors of corroded …

Corrosion phenomena and related effects, such as size reduction in both rebars and
strands, bond decay at steel–concrete interface, and cracking in the surrounding concrete …

The corrosion, main cause of degradation in RC structures in non-exceptional conditions,
can have also significant effects on the seismic behaviour, leading to dangerous strain …

This paper presents the results of an experimental study on the fatigue behavior of
pretensioned partially prestressed concrete beams with corroded prestressing wires or …

The structural behaviour of six beams subjected to different corrosion rates, under flexural
loads is analysed in the paper. Even if the corrosion consequences at local and global level …

The durability of reinforced concrete structures can be sharply reduced by the corrosion of
the steel rebars. This phenomenon is of great concern, since it is one of main cause of …

Many ageing reinforced concrete structures are affected by severe damage of reinforcing
bars due to corrosion. Accurate knowledge of the stress-strain characteristics of the installed …