The premature failure of boiler tubes, especially in coal fired boilers poses serious threat to
the efficiency of the Indian boilers. In coal fired thermal power plant boilers, hot corrosion …

The life of the components operating under various high-temperature environments
decreases due to the activation of different failure mechanisms. High-temperature oxidation …

In the present investigation, Nisingle bond20Cr and Nisingle bond5Al wires were used to
deposit coatings on T22 and SA516 boiler steels for protection in high temperature …

There are distinct types of boilers, such as fire tube boilers, water tube boilers, pulverized
fuel boilers, grate furnace boiler, oil and gas-fired boilers, fluidized bed combustion boilers …

At presently, the failure of a boiler is big hazard to the effectiveness of the boiler in the power
plants. In coal fired boilers, erosion and corrosion at high temperature is responsible for the …

High-velocity oxy fuel (HVOF) sprayed coatings can improve the corrosion resistance of bare
ASTM SA213-T22 boiler steel. In this report, we have investigated the NiCrMoFeCoAl-30 …

In the present research, the high temperature oxidation behaviour of Wire Arc sprayed Ni-
5Al coating on T-11 and Gr-A1 boiler steels was studied at 9000C for 50 cycles. Each cycle …

The primary reason of degradation and failure of many products used for high temperature
applications are oxidation. Protective coatings are employed to increase the component …

An improvement in the corrosion resistance of alloys at elevated temperature is a factor for
their potential use in gas turbines. In this study, CoNiCrAlY has been coated on the L605 …

At Mae-Moh power plant, Thailand, superheater tubes, which are exposed to a fly ash
environment, often degrade due to solid particle erosion. To extend the service lifetime of the …