Corrosion behaviors of heat-resisting alloys in high temperature carbon dioxide
L Yang, H Qian, W Kuang - Materials, 2022 - mdpi.com
The supercritical carbon dioxide Brayton cycle is a promising power conversion option for
green energies, such as solar power and nuclear reactors. The material challenge is a …
green energies, such as solar power and nuclear reactors. The material challenge is a …
Effect of pressure and impurities on oxidation in supercritical CO2
Both indirect‐and direct‐fired supercritical CO2 cycles for high‐efficiency power generation
are expected to have impurities that may greatly alter the compatibility of Fe‐and Ni‐based …
are expected to have impurities that may greatly alter the compatibility of Fe‐and Ni‐based …
Effect of Mn on oxide formation by Fe-Cr and Fe-Cr-Ni alloys in dry and wet CO2 gases at 650 C
TD Nguyen, J Zhang, DJ Young - Corrosion Science, 2016 - Elsevier
Abstract Model alloys Fe-20Cr-2Mn and Fe-20Cr-20Ni-2Mn (wt.%) were exposed to Ar-
20CO 2-(20H 2 O) gases at 650° C. Oxide formation was affected by alloy Mn diffusion …
20CO 2-(20H 2 O) gases at 650° C. Oxide formation was affected by alloy Mn diffusion …
Effects of cerium and manganese on corrosion of Fe–Cr and Fe–Cr–Ni alloys in Ar–20CO2 and Ar–20CO2–20H2O gases at 650° C
TD Nguyen, J Zhang, DJ Young - Corrosion Science, 2015 - Elsevier
Abstract Model alloys Fe–9Cr, Fe–20Cr and Fe-20Cr–20Ni (wt.%) with 0.1% Ce or 2% Mn
were exposed to Ar–20CO 2 and Ar–20CO 2–20H 2 O gas mixtures at 650° C. Ferritic alloys …
were exposed to Ar–20CO 2 and Ar–20CO 2–20H 2 O gas mixtures at 650° C. Ferritic alloys …
Temperature-dependence of oxidation and carburization of Grade 91 steel in CO2 containing impurities
Future CO 2 based power systems require steels resistant to corrosion in high-temperature
CO 2-rich environments. Candidate 9Cr ferritic-martensitic steels degrade by surface …
CO 2-rich environments. Candidate 9Cr ferritic-martensitic steels degrade by surface …
Fireside corrosion of 9Cr-1Mo steel at high temperatures, in the acid flue gas from an oil refinery
A Alviz-Meza, SI Shah, V Kafarov… - Corrosion Science, 2021 - Elsevier
The petrochemical industry is implementing practices to recover flue gases to reduce energy
waste. H 2 S in the recovered gas makes the gaseous environment acidic during reuse. This …
waste. H 2 S in the recovered gas makes the gaseous environment acidic during reuse. This …
High temperature corrosion of Fe-Cr-(Mn/Si) alloys in CO2-H2O-SO2 gases
C Yu, J Zhang, DJ Young - Corrosion Science, 2016 - Elsevier
Abstract Model alloys Fe-9Cr, Fe-20Cr (wt.%) and these alloys doped with 2% Mn or 0.5% Si
were exposed to Ar-20% CO 2-20% H 2 O-(0, 0.5)% SO 2 (vol.%) gas at 811° C for up to 500 …
were exposed to Ar-20% CO 2-20% H 2 O-(0, 0.5)% SO 2 (vol.%) gas at 811° C for up to 500 …
Effects of Si, Al and Ti on corrosion of Ni-20Cr and Ni-30Cr alloys in Ar-20CO2 at 700° C
TD Nguyen, J Zhang, DJ Young - Corrosion Science, 2018 - Elsevier
Abstract Model alloys Ni-(20, 30) Cr (wt.%) with (0.1, 1)% Si, 1.5% Al or (1, 2)% Ti were
exposed to Ar-20CO 2 at 700° C. Samples were electropolished before reaction to avoid …
exposed to Ar-20CO 2 at 700° C. Samples were electropolished before reaction to avoid …
Comprehensive insights into competitive oxidation/sulfidation reactions on binary ferritic alloys at high temperatures
C Stephan-Scherb, J Lehmusto, F Falk, O Sobol… - Corrosion …, 2022 - Elsevier
Interpreting high-temperature corrosion induced by mixed-gas atmospheres is challenging
due to the different contributions of oxidizing gases. Here, a comprehensive study on the …
due to the different contributions of oxidizing gases. Here, a comprehensive study on the …
Corrosion of Fe–9Cr–(Mn, Si) alloys in CO2–H2O–SO2 gases
C Yu, TD Nguyen, J Zhang, DJ Young - Corrosion Science, 2015 - Elsevier
Abstract Model alloys, Fe–9Cr, Fe–9Cr–2Mn and Fe–9Cr–0.5 Si (wt%) were exposed to Ar–
20% CO 2–20% H 2 O–(0, 0.1, 0.5 and 1.0%) SO 2 gases at 650° C. In the absence of SO 2 …
20% CO 2–20% H 2 O–(0, 0.1, 0.5 and 1.0%) SO 2 gases at 650° C. In the absence of SO 2 …