Rankinite binder material was synthesised from the mixture (C/S= 1.5) of locally (Lithuania)
available materials–opoka and limestone–at 1250 C for 45 min. Its suitability as a non …

Basic oxygen furnace (BOF) slag is an industrial by-product of the steel industry and is
currently used only in low-end applications like road fill or is landfilled. This study explores …

The main measure to reduce energy losses is the usage of insulating materials. When the
temperature exceeds 500° C, silicate and ceramic products are most commonly used. In this …

In this work the possibility of producing a CO 2 hardened concrete where the binder is a
calcium silicate hydrate instead of anhydrous silicates was investigated and the …

In this work, the peculiarities of the formation of 1.13 nm tobermorite using both natural raw
materials (decalcinated limestone and opoka) and chemically pure reagents (CaO, SiO 2· H …

The influence of aluminum additive on the formation mechanism and thermal stability of
calcium silicate hydrates was determined. Calcium silicates hydrates were synthesized in …

Abstract [eng] This study presents the peculiarities that occur during the hydrothermal
synthesis of 1.13 nm tobermorite from granite sawing powder waste and CaO. The molar …

In this work, a combined method of using DSC, TG and XRD analysis in order to determine
an amount of decomposed α-C 2 SH in its tribochemically activated mixture with quartz is …

In this work, the results of preparing a novel hydraulic binder material on α-C 2 SH basis
using both chemically pure and natural raw materials are presented, as well as hydration …

The influence of aluminum additive on the formation of α-C 2 SH and on kinetics of
cementitious binder material at early stages of hydration was determined. α-C 2 SH was …