Corrosion resistance of WC hardmetals with different Co and Ni-based binders
P Pereira, AMF Rocha, J Sacramento… - International Journal of …, 2022 - Elsevier
In this work, industrially relevant WC composites with alternative binders (Ni, CoNi, NiCr,
CoCr, CoNiCr and NiCrMo) were produced and their corrosion resistance in 0.5 M NaCl was …
CoCr, CoNiCr and NiCrMo) were produced and their corrosion resistance in 0.5 M NaCl was …
Tribocorrosion of TiC-based composites incorporating Ni and Co binders in saline solutions
Metallic binders impart necessary toughness to ceramic-metal composites, yet are
vulnerable to corrosion and wear. Thus far, the tribocorrosion mechanism remains little …
vulnerable to corrosion and wear. Thus far, the tribocorrosion mechanism remains little …
[HTML][HTML] Stripping process of TiAlN/TiSiN coating on WC-Co cemented carbide substrate by using the dry-electropolishing technique
Abstract Physical Vapor Deposition hard protective coatings are frequently applied to
hardmetal cutting tools to extend their lifespan under service-like working conditions …
hardmetal cutting tools to extend their lifespan under service-like working conditions …
[HTML][HTML] Thermomechanical behaviour of WC-W2C composites at first wall in fusion conditions
EM Garcia-Ayala, S Tarancon, B Ferrari… - International Journal of …, 2021 - Elsevier
Metallic tungsten and tungsten carbide are some of the more relevant candidates proposed
because of their high melting point, shielding capabilities and resistance to neutron damage …
because of their high melting point, shielding capabilities and resistance to neutron damage …
The corrosion performance for ultrafine WC-12Co processed by heat treatments in different pH solutions
The corrosion performance of WC-12Co after different post heat treatments (1100° C, 1100°
C+ 400° C, 1100° C+ 500° C, 1100° C+ 600° C), were tested in 0.05 MH 2 SO 4, 0.1 M Na 2 …
C+ 400° C, 1100° C+ 500° C, 1100° C+ 600° C), were tested in 0.05 MH 2 SO 4, 0.1 M Na 2 …
Corrosion-induced changes on Hertzian contact damage in cemented carbides
In this study, the influence of corrosion on the mechanical response and damage induced
under Hertzian indentation is assessed for three cemented carbides with metallic binders of …
under Hertzian indentation is assessed for three cemented carbides with metallic binders of …
Effect of binder nature and content on the cavitation erosion resistance of cemented carbides
O Lavigne, N Cinca, O Ther, E Tarrés - International Journal of Refractory …, 2022 - Elsevier
Cavitation erosion is a common mode of wear in flow control and fluid handling systems. To
mitigate this degradation mode, Cosingle bondCr superalloys or facing coatings are …
mitigate this degradation mode, Cosingle bondCr superalloys or facing coatings are …
[HTML][HTML] Contact fatigue of WC-6% wtCo cemented carbides: Influence of corrosion-induced changes on emergence and evolution of damage
The effect of corrosion-induced changes on the contact fatigue response and associated
damage in a medium-grained WC-6% wtCo hardmetal grade is investigated. Cyclic contact …
damage in a medium-grained WC-6% wtCo hardmetal grade is investigated. Cyclic contact …
Indentation and scratch testing of a WC-6% wtCo cemented carbide: Corrosion effects on load-bearing capability and induced damage
In this work, corrosion effects on the indentation and scratch response of a WC-6% Co
hardmetal are investigated. Experimental variables include relative long corrosion times as …
hardmetal are investigated. Experimental variables include relative long corrosion times as …
Electrochemical Corrosion Characterization of Submicron WC-12Co Coatings Produced by CGS and HVAF Compared with Sintered Bulks
The electrochemical corrosion performance of WC-12 wt% Co in coating and bulk forms has
been evaluated in a 3.56 wt% NaCl solution. The coatings were deposited by means of …
been evaluated in a 3.56 wt% NaCl solution. The coatings were deposited by means of …