Deformation behavior of plastic zone at crack tip of 304 stainless steel
T Sun, Y Zhu, Y Deng - … & Fracture of Engineering Materials & …, 2024 - Wiley Online Library
In this paper, the deformation behavior of plastic zone at crack tip during crack propagation
of 304 stainless steel was studied. Firstly, the fatigue crack propagation tests of 304 stainless …
of 304 stainless steel was studied. Firstly, the fatigue crack propagation tests of 304 stainless …
Theoretical Estimation of Fatigue Life before Crack Initiation in Metal Materials at Variable Cycle Stresses
OM Herasymchuk, OV Kononuchenko - Strength of Materials, 2024 - Springer
A model is proposed to theoretically evaluate fatigue life (number of loading cycles) until the
moment of fatigue crack initiation (duration of stage 1 of fatigue failure) in specimens with a …
moment of fatigue crack initiation (duration of stage 1 of fatigue failure) in specimens with a …
Model of Short Fatigue Crack Growth Rate and Fatigue Life Estimation of Carbon Steel Specimens
OM Herasymchuk, O Kononuchenko - Strength of Materials, 2023 - Springer
This study proposed a model describing the kinetics of short fatigue crack growth from a
smooth surface and from the top of a blunt notch. The driving force of the fatigue crack is the …
smooth surface and from the top of a blunt notch. The driving force of the fatigue crack is the …
Correlation Characteristics of the Deformation Relief of an Aluminum Alloy Under High-Cycle Fatigue
GG Pysarenko, AV Byalonovych, LE Matokhnyuk… - Strength of …, 2024 - Springer
The mechanical properties, alloy microstructure, and fatigue resistance under cyclic loading
of a 1.5 mm thick D16 sheet with a stress concentrator in the form of a central hole were …
of a 1.5 mm thick D16 sheet with a stress concentrator in the form of a central hole were …