[HTML][HTML] Microstructural and mechanical properties of Al-Zn alloy 7075 during RRA and triple aging
Since aluminum is used in many essential applications, it has become a focus of
researchers, mainly aluminum alloy 7075, because of its importance in the aircraft industry …
researchers, mainly aluminum alloy 7075, because of its importance in the aircraft industry …
Effects of Sc and Zr microalloying additions and aging time at 120 C on the corrosion behaviour of an Al–Zn–Mg alloy
Y Deng, Z Yin, K Zhao, J Duan, J Hu, Z He - Corrosion Science, 2012 - Elsevier
Sc and Zr microalloying additions and increasing aging time at 120° C both can effectively
improve the corrosion resistance of Al–Zn–Mg alloys. The low corrosion susceptibility …
improve the corrosion resistance of Al–Zn–Mg alloys. The low corrosion susceptibility …
Influence of retrogression and re-aging treatment on corrosion behaviour of an Al–Zn–Mg–Cu alloy
YP Xiao, QL Pan, WB Li, XY Liu, YB He - Materials & Design, 2011 - Elsevier
Influence of retrogression and re-aging treatment on the microstructure, strength, exfoliation
corrosion, inter-granular corrosion and stress corrosion cracking of an Al–Zn–Mg–Cu alloy …
corrosion, inter-granular corrosion and stress corrosion cracking of an Al–Zn–Mg–Cu alloy …
The effects of aging treatments on mechanical property and corrosion behavior of spray formed 7055 aluminium alloy
LL Liu, QL Pan, XD Wang, SW Xiong - Journal of Alloys and Compounds, 2018 - Elsevier
The relationship among microstructures, mechanical properties and corrosion behaviors of
spray formed 7055 aluminium alloy has been investigated upon peak-aging (T6), double …
spray formed 7055 aluminium alloy has been investigated upon peak-aging (T6), double …
Microstructure, mechanical performance, and corrosion behavior of additively manufactured aluminum alloy 5083 with 0.7 and 1.0 wt% Zr addition
Abstract Effect of 0.7 wt% and 1.0 wt% of Zr alloying on the laser powder bed fused (LPBF)
printability/buildability of AA5083 alloys was investigated by examination of the …
printability/buildability of AA5083 alloys was investigated by examination of the …
Effect of Sc and Zr additions on corrosion behaviour of Al–Zn–Mg–Cu alloys
Y Shi, Q Pan, M Li, X Huang, B Li - Journal of Alloys and Compounds, 2014 - Elsevier
In this paper, the relationship between recrystallization and corrosion behaviour of Al–Zn–
Mg–Cu alloys has been investigated. The additions of Sc and Zr inhibited the …
Mg–Cu alloys has been investigated. The additions of Sc and Zr inhibited the …
Mechanism of low exfoliation corrosion resistance due to slow quenching in high strength aluminium alloy
SD Liu, B Chen, CB Li, Y Dai, YL Deng, XM Zhang - Corrosion Science, 2015 - Elsevier
Electrochemical impedance spectroscopy and accelerated immersion testing results
indicate that a lower quench rate leads to lower exfoliation corrosion resistance in 7055 …
indicate that a lower quench rate leads to lower exfoliation corrosion resistance in 7055 …
铝合金的晶间腐蚀与剥蚀
苏景新, 张昭, 曹发和, 张鉴清, 曹楚南 - 中国腐蚀与防护学报, 2009 - jcscp.org
综述了近几十年来国内外在2xxx 系和7xxx 系铝合金及Al-Li 合金的晶间腐蚀和剥蚀等研究方面
的主要进展. 总结了合金中晶界沉淀相的成分, 分布及其与晶格的击穿电位差异等对晶间腐蚀的 …
的主要进展. 总结了合金中晶界沉淀相的成分, 分布及其与晶格的击穿电位差异等对晶间腐蚀的 …
Effect of repetitious non-isothermal heat treatment on corrosion behavior of Al-Zn-Mg alloy
Type 7N01 alloy has been widely applied in rail vehicles, but corrosion behavior and
mechanical properties of this alloy after heat treatment or heat straightening becomes a …
mechanical properties of this alloy after heat treatment or heat straightening becomes a …
Three-stage degradation behavior and dealloying assisted galvanic corrosion mechanism of 300 MPa grade Zn-2Cu-xLi (x= 0.2-0.8) alloys in simulated body fluid
M Cao, ZZ Shi, JL Sun, Z Li, LN Wang - Corrosion Science, 2024 - Elsevier
Corrosion behaviors of biodegradable Zn alloys with ternary phases are rarely studied. This
paper reveals three-stage corrosion behavior of high-strength Zn-2Cu-(0.2–0.8) Li alloys …
paper reveals three-stage corrosion behavior of high-strength Zn-2Cu-(0.2–0.8) Li alloys …