δ-Bi2O3: M (M= S, Se, and Re) with an oxygen-defective fluorite-type structure is obtained
by a coprecipitation method starting from the bismuth oxido cluster [Bi38O45 (OMc) 24 …

Abstract The Cs 2 MoO 4 single crystal grown by the Czochralski method was characterized
using X-ray diffraction analysis and its heat capacity was measured by differential scanning …

The substitution of Re into Bi 2 O 3 allows stabilization of the δ-Bi 2 O 3 structure by
additional substitution of lutetium ion to give phase of composition Bi 12.5 Lu 1.5 ReO 24.5 …

An investigation of the interaction of Bi (III) with an aqueous solution of sulfanilic acid at a
higher temperature is performed. As a result, a new composition [Bi6O6 (OH) …

On the basis of experimental data the lattice energies for the new compounds Bi 12.5 Ln 1.5
ReO 24.5 have been calculated using a Born–Haber cycle. It has been discovered that there …

The heat capacity of Bi 12.5 Lu 1.5 ReO 24.5 was measured for the first time in the
temperature range of 175–550 K. Calorimetric experiments were performed using …

The Bi12. 5Dy1. 5ReO24. 5 phase has been prepared from Bi2O3, Dy2O3, and Re2O7. X-
ray measurements have showed that Bi12. 5Dy1. 5ReO24. 5 has a cubic structure (Fm3m …

For the first time solution enthalpies of BaCe 0.8 Y 0.1 Gd 0.1 O 2.9, BaCe 0.8 Y 0.1 Lu 0.1 O
2.9 and mixtures of BaCl 2+ 0.8 CeCl 3+ 0.1 YCl 3+ 0.1 GdCl 3, BaCl 2+ 0.8 CeCl 3+ 0.1 YCl …

Solution calorimetry, using 1 mol dm− 3 HCl as a solvent, has been used to study for the first
time the thermochemistry of Bi 2.67 Er 0.33 CoO 5.83. For the first time, the standard …

Solution enthalpies of barium cerate doped by gadolinium and indium and a mixture of BaCl
2+ 0.7 CeCl 3+ 2GdCl 3+ 0.1 InCl 3 have been measured in 1 mol dm− 3 HCl with 0.1 mol …