Peculiarities of short fatigue cracks growth from a blind hole in specimens made of steel 45. Part 1. Experimental results
OM Herasymchuk, OV Kononuchenko - Strength of Materials, 2021 - Springer
Results of in situ measurements of short fatigue cracks growth from a blind hole of diameter
0.6 and 1.6 mm in specimens from steel 45 during cyclic loading at different cycle asymmetry …
0.6 and 1.6 mm in specimens from steel 45 during cyclic loading at different cycle asymmetry …
Microstructure-based model for sharp stress raiser-related fatigue stage length assessment
OM Herasymchuk, AI Novikov - Strength of Materials, 2019 - Springer
A model for evaluating the fatigue life of specimens/structure elements with sharp stress
raisers/defects is presented. The model permits of computing the number of cycles to fatigue …
raisers/defects is presented. The model permits of computing the number of cycles to fatigue …
The range of use of the critical distance concept to predict the endurance limit in the presence of stress raisers
OM Herasymchuk, OV Kononuchenko - Strength of Materials, 2020 - Springer
The paper presents results of fatigue tests in the tension–compression and tension–tension
modes of specimens of 45 steel: smooth specimens and specimens with a blind hole of …
modes of specimens of 45 steel: smooth specimens and specimens with a blind hole of …
[PDF][PDF] РОЗРОБЛЕННЯ МОДЕЛЕЙ РОСТУ КОРОТКИХ ТРІЩИН У МЕТАЛЕВИХ МАТЕРІАЛАХ ЗА ТРИВАЛИХ НАВАНТАЖЕНЬ ТА ЕКСПЛУАТАЦІЙНИХ …
НС Яджак - lnu.edu.ua
Дисертація присвячена дослідженню поширення коротких втомних тріщин у металевих
матеріалах та математичному моделюванню їх росту. Метою дисертаційної роботи є …
матеріалах та математичному моделюванню їх росту. Метою дисертаційної роботи є …