Crack initiation mechanisms during very high cycle fatigue of Ni-based single crystal superalloys at high temperature
Crack initiation mechanisms in the very high cycle fatigue (VHCF) regime of nickel-based
single-crystal (SX) superalloys have been investigated at high temperature (1000° C) and …
single-crystal (SX) superalloys have been investigated at high temperature (1000° C) and …
Diversity of damage evolution during cyclic loading at very high numbers of cycles
M Zimmermann - International Materials Reviews, 2012 - Taylor & Francis
Over the last decade, it has been shown for a number of metals that failure occurs even
beyond the classical fatigue limit. High frequency testing techniques make it possible to …
beyond the classical fatigue limit. High frequency testing techniques make it possible to …
Coupling effects of microstructure and defects on the fatigue properties of laser powder bed fusion Ti-6Al-4V
Z Qu, ZJ Zhang, YK Zhu, R Liu, SL Lu, SJ Li… - Additive …, 2023 - Elsevier
The coupling effects of microstructure and macro-scale defects are significant for the fatigue
properties of metallic materials. However, this correlation is still vague for additively …
properties of metallic materials. However, this correlation is still vague for additively …
A comprehensive study on the fatigue properties of duplex surface treated Ti6Al4V by plasma nitriding and DLC coating
This study aims to investigate the effects of duplex surface treatment consisting of plasma
nitriding and DLC coating on the fatigue properties of Ti6A4V alloy. For this investigation …
nitriding and DLC coating on the fatigue properties of Ti6A4V alloy. For this investigation …
Crack initiation mechanisms under two stress ratios up to very-high-cycle fatigue regime for a selective laser melted Ti-6Al-4V
Crack initiation mechanisms under two stress ratios (R=− 1 and 0.5) and up to very-high-
cycle fatigue (VHCF) regime of a selective laser melted (SLMed) Ti-6Al-4V were …
cycle fatigue (VHCF) regime of a selective laser melted (SLMed) Ti-6Al-4V were …
The effect of microstructure on the mechanical properties of TC4-DT titanium alloys
P Guo, Y Zhao, W Zeng, Q Hong - Materials Science and Engineering: A, 2013 - Elsevier
This paper presents the results on the microstructure and mechanical properties of damage
tolerance TC4-DT titanium alloy after different heat treatments. The influence of volume …
tolerance TC4-DT titanium alloy after different heat treatments. The influence of volume …
Crack initiation mechanisms of Ti6Al4V in the very high cycle fatigue regime
S Heinz, D Eifler - International Journal of Fatigue, 2016 - Elsevier
High frequency fatigue tests were carried out with a 20 kHz ultrasonic testing facility to
investigate the cyclic deformation behavior of Ti6Al4V in the Very High Cycle Fatigue …
investigate the cyclic deformation behavior of Ti6Al4V in the Very High Cycle Fatigue …
The behavior of crack initiation and early growth in high-cycle and very-high-cycle fatigue regimes for a titanium alloy
X Pan, H Su, C Sun, Y Hong - International Journal of Fatigue, 2018 - Elsevier
The behavior of crack initiation and early growth in high-cycle fatigue (HCF) and very-high-
cycle fatigue (VHCF) regimes for a TC4 titanium alloy with equiaxed microstructure was …
cycle fatigue (VHCF) regimes for a TC4 titanium alloy with equiaxed microstructure was …
Non-destructive observation of internal fatigue crack growth in Ti–6Al–4V by using synchrotron radiation μCT imaging
F Yoshinaka, T Nakamura, S Nakayama… - International Journal of …, 2016 - Elsevier
The propagation of an internal fatigue crack in Ti–6Al–4V was non-destructively observed by
synchrotron radiation μCT imaging to clarify the crack growth rate in very high cycle fatigue …
synchrotron radiation μCT imaging to clarify the crack growth rate in very high cycle fatigue …
Analysis of fatigue properties and failure mechanisms of Ti6Al4V in the very high cycle fatigue regime using ultrasonic technology and 3D laser scanning vibrometry
Accelerated fatigue tests with Ti6Al4V were carried out using a 20 kHz ultrasonic testing
facility to investigate the cyclic deformation behavior in the Very High Cycle Fatigue (VHCF) …
facility to investigate the cyclic deformation behavior in the Very High Cycle Fatigue (VHCF) …