Abstract Mn rich Ni-Mn-Sn and Ni-Mn-Co-Sn alloy films were deposited on Si (1 0 0)
substrate by dc magnetron sputtering from Ni 50 Mn 37 Sn 13 alloy target at 1.8 Pa Ar …

Pressure study of the Heusler Ni 2 MnSn-based alloys revealed divergent values of the
pressure effects on magnetic properties within a group of the off-stoichiometric alloys. An …

Amorphous TbFeCo thin films sputter deposited at room temperature on thermally oxidized
Si substrate are found to exhibit strong perpendicular magnetic anisotropy. Atom probe …

The fabrication of high-quality Heusler alloy films with clear martensitic transformation is a
challenging issue in the field of magnetic shape memory alloys. Here, flexible Mn-rich Ni …

In this work, a giant exchange bias field of over 1 kOe, which is uncommon in film systems, is
obtained in all-3d-metal Heusler-type Ni 38.8 Co 2.9 Mn 37.9 Ti 20.4 thin films. The …

We report a perpendicular magnetic tunnel junction (pMTJ) cell with a tunnel
magnetoresistance (TMR) ratio of nearly 200% at room temperature based on …

Amorphous ferrimagnetic TbFeCo thin films are found to exhibit exchange bias effect near
the compensation temperature by magnetic hysteresis loop measurement. The observed …

Abstract Off-stoichiometric Mn-rich Ni-Mn-Sn films of different thicknesses were deposited on
Si (100) substrate by dc magnetron sputtering at ambient temperature and then annealed ex …

Abstract Cu or Fe or Co substituted off-stoichiometric Ni-Mn-Sn films of 500 nm thickness
were deposited on Si (1 0 0) substrate by dc magnetron sputtering at ambient temperature …

Abstract In this work, Ni-Co-Mn-Ti ferromagnetic shape memory alloy thin films, which
consists of all 3d metals, are well prepared by direct-current (DC) double targets magnetron …