Hydrogen embrittlement in ferritic steels
Hydrogen will be a crucial pillar in the clean-energy foundation, and therefore, the
development of safe and cost-effective storage and transportation methods is essential to its …
development of safe and cost-effective storage and transportation methods is essential to its …
The experiment study to assess the impact of hydrogen blended natural gas on the tensile properties and damage mechanism of X80 pipeline steel
D Zhou, T Li, D Huang, Y Wu, Z Huang, W Xiao… - International Journal of …, 2021 - Elsevier
Environmental hydrogen embrittlement has become a non-negligible problem in the
hydrogen blended natural gas transportation. To qualitatively study the degradation …
hydrogen blended natural gas transportation. To qualitatively study the degradation …
Interfacial mechanical behavior in nacre of red abalone and other shells: a review
Interfaces between nacreous tablets are crucial to the outstanding mechanical properties of
nacre in natural shells. Excellent research has been conducted to probe the effect of …
nacre in natural shells. Excellent research has been conducted to probe the effect of …
Hydrogen permeation and embrittlement susceptibility of X80 welded joint under high-pressure coal gas environment
W Zhao, T Zhang, Y Zhao, J Sun, Y Wang - Corrosion Science, 2016 - Elsevier
Hydrogen permeation and slow strain rate tests in a high-pressure hydrogen-containing coal
gas, combined with microstructural analysis, were conducted on X80 base metal, weld …
gas, combined with microstructural analysis, were conducted on X80 base metal, weld …
Deposition of Ni–NiO nanoparticles on the reduced graphene oxide filled polypyrrole: evaluation as cathode catalyst in microbial fuel cells
P Pattanayak, F Papiya, N Pramanik… - Sustainable Energy & …, 2019 - pubs.rsc.org
Herein, we fabricated the in situ polymerization of pyrrole (Py) on reduced graphene oxide
(rGO), formulated as a nanocomposite support matrix for the deposition of nickel–nickel …
(rGO), formulated as a nanocomposite support matrix for the deposition of nickel–nickel …
Effect of microstructure inhomogeneity on hydrogen embrittlement susceptibility of X80 welding HAZ under pressurized gaseous hydrogen
Hydrogen embrittlement (HE) of high-grade pipeline welded joint is a threat to hydrogen gas
transport. In this research, slow strain rate tension (SSRT) tests in high-pressure hydrogen …
transport. In this research, slow strain rate tension (SSRT) tests in high-pressure hydrogen …
Fracture toughness of coarse-grain heat affected zone of quenched and tempered CrMo steels with internal hydrogen: Fracture micromechanisms
The determination of fracture behaviour of welds in presence of internal hydrogen is
essential for the integrity assessment of CrMo vessels and pipes working under high …
essential for the integrity assessment of CrMo vessels and pipes working under high …
Hydrogen blistering and cracking of high-strength pipeline steel welds produced by electrochemical hydrogen charging
Pipeline steel system always faces a challenge of hydrogen embrittlement (HE) not only due
to corrosion environments but also because of cathodic protection strategy. Especially in …
to corrosion environments but also because of cathodic protection strategy. Especially in …
Hydrogen embrittlement in dissimilar welded joints interfaces–Influence of manufacturing parameters and evaluation of methodologies
MGM de Carvalho, MA Lage… - Corrosion …, 2023 - Elsevier
The resistance of dissimilar joints to hydrogen was assessed using fracture toughness in an
aggressive environment and slow strain rate tests. Six weld joint conditions were evaluated …
aggressive environment and slow strain rate tests. Six weld joint conditions were evaluated …
Effect of heat treatment on hydrogen-assisted fracture behavior of PH13-8Mo steel
Abstract Effect of heat treatment on hydrogen-assisted fracture behavior of PH13-8Mo steel
was investigated. The results show that hydrogen embrittlement susceptibility of the …
was investigated. The results show that hydrogen embrittlement susceptibility of the …