Environmental degradation of structural materials in liquid lead-and lead-bismuth eutectic-cooled reactors
Liquid lead (Pb)-and lead–bismuth eutectic (LBE)-cooled fast neutron reactors (Gen-IV
LFRs) are one of the most technologically mature fission reactor technologies, due to their …
LFRs) are one of the most technologically mature fission reactor technologies, due to their …
Effects of radiation-induced defects on corrosion
The next generation of nuclear reactors will expose materials to conditions that, in some
cases, are even more extreme than those in current fission reactors, inevitably leading to …
cases, are even more extreme than those in current fission reactors, inevitably leading to …
Proton irradiation-decelerated intergranular corrosion of Ni-Cr alloys in molten salt
The effects of ionizing radiation on materials often reduce to “bad news”. Radiation damage
usually leads to detrimental effects such as embrittlement, accelerated creep, phase …
usually leads to detrimental effects such as embrittlement, accelerated creep, phase …
Influence of Gamma-Irradiation on Structural, Optical and Photocatalytic Performance of TiO2 Nanoparticles Under Controlled Atmospheres
The effect of gamma-rays on structural, optical and photocatalytic properties of TiO 2
nanoparticles under controlled atmospheres are studied to further improve photocatalytic …
nanoparticles under controlled atmospheres are studied to further improve photocatalytic …
In-situ proton irradiation/lead-bismuth eutectic corrosion synergistic effect on corrosion behaviour of 11Cr1W1Si ferritic/martensitic steel
Q Chen, Y Chen, F Zhang, J Yang, C Zhu… - Journal of Nuclear …, 2023 - Elsevier
In-situ proton irradiation/lead-bismuth eutectic corrosion synergistic effect on corrosion
behaviour of 11Cr1W1Si ferritic/martensitic steel was investigated. The result indicated that …
behaviour of 11Cr1W1Si ferritic/martensitic steel was investigated. The result indicated that …
Accelerated corrosion of FeCrAlTi coating by in situ proton irradiation in molten lead-bismuth eutectic
J Yang, Y Zhong, R Wang, W Zhang, J Yang - Corrosion Science, 2024 - Elsevier
The synergistic effect of simultaneous proton irradiation and LBE corrosion on FeCrAlTi
coating is investigated, and the surface morphology, elementary composition, microstructure …
coating is investigated, and the surface morphology, elementary composition, microstructure …
Complexity of segregation behavior at localized deformation sites formed while in service in a 316 stainless steel baffle-former bolt
Post-irradiation evaluation was performed on a 316 stainless steel baffle former bolt
harvested after 40 years of service in a pressurized water reactor. Microstructure analysis …
harvested after 40 years of service in a pressurized water reactor. Microstructure analysis …
HLMIF, a facility for investigating the synergistic effect of ion-irradiation and LBE corrosion
C Yao, Z Wang, H Zhang, H Chang, Y Sheng… - Journal of Nuclear …, 2019 - Elsevier
The synergistic effect of irradiation and Lead Bismuth Eutectic (LBE) corrosion on structural
materials is of vital importance for the research and development of future lead cooled …
materials is of vital importance for the research and development of future lead cooled …
Effects of simultaneous proton irradiation on the corrosion of commercial alloys in molten fluoride salt
Molten salt fission and fusion reactors hold promise for large-scale, carbon-free power
generation, but only if the combined effects of simultaneous irradiation and corrosion on …
generation, but only if the combined effects of simultaneous irradiation and corrosion on …
Corrosion-driven outward migration and growth of helium bubbles in a nickel-based alloy in high-temperature molten salt environment
G Lei, S Yang, H Huang, Q Huang, R Liu, W Zhang… - Corrosion …, 2019 - Elsevier
High-temperature helium ion irradiation was conducted on a nickel-based alloy at 650° C. A
unique outward migration of helium bubbles was observed in the irradiated alloy under …
unique outward migration of helium bubbles was observed in the irradiated alloy under …