Commercially available constantan alloy rods (nominal composition Cu55–Ni44–Mn1 wt%)
have been thermo-mechanically processed to develop biaxially textured substrates. It was …

Two copper based biaxially textured alloys containing 0.37 and 0.91 wt.%‐Fe have been
investigated for the use as substrate material for coated conductors. Average full width at …

Ni–Cu–Co alloys were studied for the development of textured substrates for YBCO-coated
conductor application. Three compositions were obtained by adding a fixed amount of 3at …

A sharp cubic texture is formed in a number of copper alloys subjected to cold deformation
by rolling by 98.6–99% followed by recrystallization annealing, which opens up fresh …

The crystallographic texture, micro-hardness and magnetic property have been investigated
in Cu-57 at.% Ni, Cu-53 at.% Ni, and Cu-49 at.% Ni alloy used as substrates for coated …

It has been shown that, in some copper-based alloys subjected to cold deformation by
rolling to 98.6–99% followed by recrystallization annealing, a sharp cube texture can be …

В ряде медных сплавов после холодной деформации прокаткой на 98.6− 99% и
рекристаллизационного отжига получена острая кубическая текстура, что открывает …

Ni-5 at.% W (Ni5W) tapes with a strong cube texture were fabricated using the RABiTS
technique and by starting from cylindrical shaped ingots. In contrast to a conventional cuboid …

Here, we demonstrate heteroepitaxial growth of MgO/TiN thin films on flexible metal foil of
copper substrates using pulsed laser deposition. X-ray and electron diffraction …

Показано, что в ряде медных сплавов после холодной деформации прокаткой на 98.6
99% и последующего рекристаллизационного отжига можно получить острую …