The effect of temperature on the passive film structure and corrosion performance of
CoCrFeMoNi HEA was studied. The results indicated that the passive films exhibited a …

The effect of high temperature on the corrosion behaviour and passive film composition of
316 L stainless steel in high H 2 S-containing environments was investigated. The results …

The microstructural evolution and corrosion performance in chloride environments of as-cast
AlCrFeNi 3 Mo x (x= 0, 0.1, 0.2, 0.3, and 0.4 in molar ratio) high-entropy alloys (HEAs) were …

The corrosion behavior and surface characterization of an equiatomic CoCrFeMoNi high-
entropy alloy (HEA) under various pH conditions were investigated by Mott–Schottky …

Abstract The influence of temperature (25, 75, and 150° C) on the passivation behavior of
Modified Martensitic 13Cr Stainless Steel (M13Cr) in CO 2 saturated acidic salt brine …

Corrosion would lead to the failure of materials during service, causing huge economic
losses and catastrophic accidents, particularly in chemical industries. In this work, a series of …

With suitable thermophysical properties and commercial viability, molten chlorides are
promising candidates to replace nitrate salts as heat transfer fluids (HTF) and thermal …

The microstructure and oxidation behavior of Laser Beam Melted, Electron Beam Melted
and wrought Hastelloy X were studied at 950° C in dry air, 50 h cycles, up to 1000 h. The …

The comprehensive effects of high temperatures and corrosive environments tend to cause
grievous damage to the workpieces. In this paper, the effect of high temperature on the …

Abstract Model alloy, Fe-20Cr (wt%), was exposed in Ar-(5, 20) H 2 O, Ar-(5, 20) H 2 O-5H 2
and Ar-20O 2 (vol%) at 750 and 850° C. The alloy formed Cr 2 O 3 scales plus Fe-rich oxide …