Isothermal compression tests of a new type Al–Zn–Mg–Er–Zr alloy are carried out on a
Gleeble-3800 thermal simulator at temperatures varying from 300 to 460° C and strain rates …

The hot deformation behavior of an Al-Mg-Si-Zr-Mn alloy was investigated by performing
uniaxial compression tests over a temperature range of 400–550° C and strain-rate range of …

The effects of homogenization treatments on the precipitation behavior of Al 3 (Er, Zr)
particles and theirs effects on recrystallization resistance in a new type Al-Zn-Mg-Er-Zr alloy …

Phase transformation during annealing in rapidly-solidified Al-Zn-Mg-Cu alloy was
investigated by differential scanning calorimetry, X-ray diffraction, transmission electron …

The effects of La addition on the microstructure, thermal conductivity and mechanical
properties of as-cast and as-extruded Mg-3Al-xLa-0.3 Mn (x= 1, 3 and 5 wt.%) alloys were …

The effects of homogenization on dissolution and precipitation behaviors of intermetallic
phase in a novel Zr and Er containing Al–Zn–Mg–Cu alloy were investigated. In this work …

This research concerns the effect of homogenization treatment on the electrical resistivity of
AA7020 aluminum alloy variants with different Zr and Cr contents. Small changes in the Zr …

The evolution of the eutectic structures in the as-cast and homogenized 7X50 aluminum
alloys was studied by scanning electron microscopy (SEM), transmission electron …

The effects of three-stage homogenization on recrystallization and fatigue crack growth
behavior of 7020 aluminum alloy were investigated. It was shown that a large amount of fine …

The isothermal hot compression tests of as-cast and homogenized 2024 aluminum alloy
were carried out under wide range of deformation temperatures (623-773 K) and strain rates …