Cu/Al laminated composite was fabricated by means of asymmetrical roll bonding and
annealing process. The interfacial microstructure and mechanical properties of clad sheets …

Friction stir welding (FSW) joints are inevitably accompanied with the change in shape of the
abutting surfaces due to the tool movement. Further, the formation of brittle intermetallics …

Currently, there are few works devoted to the change in the microstructure of steel-copper
bimetallic wire during its deformation. Since steel and copper have different mechanical …

In the present study, the bimetal composite rods composed of a softer AZ31 sleeve and a
harder WE43 core were fabricated via a special process by combining hot-pressing diffusion …

Equal-channel angular pressing (ECAP) was used to fabricate Al/steel bimetallic rod for
potential application in overhead transmission conductors. Bimetallic rods consisted of an …

Joint interface and cracking mechanism during thick cladding of copper on aluminum have
been investigated. For this purpose, deformation of Al-Cu bimetallic inserts during equal …

Abstract STS439/Al1050/STS304 clad composite with high specific strength and high
bending resistance was processed and its formability and interface fracture behavior of as …

The superior properties of ultrafine-grained materials fabricated by severe plastic
deformation (SPD) have attracted the attention of many researchers around the world …

The effects of interfacial modification in tri-layered Cu/Al/Cu composites by heat treatment on
interface stability and crack propagation were investigated. In order to investigate the crack …

The Cu/Al composites conductive head is widely used in hydrometallurgy as the core
component of cathode plate. Its conductive properties directly affect the power consumption …