CrN and CrCN coatings were deposited by the cathodic arc ion plating technique.
Microstructures, mechanical properties and tribological performances of the CrN and CrCN …

In this study, a high-power Nd: YAG laser is used to remove a corrosion layer on the surface
of 304L stainless steel (SS304L). A laser power of 1140 W with different hatch distances and …

The CrN (C) coatings with different carbon contents were deposited using unbalanced
magnetron sputtering via adjusting the carbon target current, and their microstructure and …

Chromium carbide films with different phase contents were deposited at 126±26° C by
industrial high rate reactive magnetron sputtering, using both direct current magnetron …

Hard ceramic and ductile metal materials combined in multilayered structures provide
superior wear and oxidation resistance to the single layer, which has been applied …

It is known that mechanical and tribological properties of transition metal carbide films can
be tailored by adding an amorphous carbon (aC) phase, thus making them nanocomposites …

Chromium carbide coating on steel is a good candidate for applications on forming and
molding dies. The high mechanical strength, chemical resistance and high temperature …

Abstract CrCx coatings (where x= 5~ 35 sccm is the acetylene flux) were deposited on
stainless steel 316L substrates using radio frequency unbalanced magnetron sputtering …

In the present work, production of the chromium carbide was investigated by reduction of
chromium oxide with methane-containing gas mixture. The experiments were conducted on …

Corrosion testing of UNS N10003 in molten fluoride salt was performed in purified molten
27LiF-BeF2 (66–34 mol%)(FLiBe) salt at 700° C for 1,000 h, in pure nickel and graphite …