Fatigue-creep tests were carried out on bare and salt-coated of DZ125 superalloys samples
at 850° C. The fatigue lifetime of a corroded alloy was reduced by more than 80% as the …

Abstracts Low cycle fatigue behavior of the superalloy IN718 was studied with Type-A (Na 2
SO 4+ NaCl) and Type-B (Na 2 SO 4+ NaCl+ V 2 O 5) salt coatings, at 650° C in total strain …

The effect of NaCl deposition on the deformation and fracture behavior during the cycle
loading of dwell fatigue of Ti-6Al-4V alloy at 500° C was investigated. Experimental results …

The effects of Fe content on microstructure, thermal stability and tensile properties of a Ni–Fe–
Cr based superalloy, mainly chosen as turbine rotor material in 700° C advanced ultra …

High cycle fatigue behavior of the superalloy IN718 was studied in the air at 600° C in fully
reversed stress controlled mode (R=− 1), in the as heat treated condition as well as pre hot …

Установлено, что для оценки стойкости сплавов к сульфидно-оксидной коррозии (СОК)
в основном используют три вида испытаний: стендовые, в печах и электрохимические …

Creep-rupture behaviour of IN718 with deposit of 87.5 wt.% Na 2 SO 4+ 5 wt.% NaCl+ 7.5
wt.% NaVO 3 (3SM) in the stress range of 550–850 MPa at 650° C is investigated. 3SM …

对于沿海地区或海洋环境中使用的航空发动机来说, 由于高温, 机械载荷和盐雾环境的共同作用,
热腐蚀疲劳破坏是影响其热端部件服役寿命的主要因素. 本文对热端部件低温热腐蚀疲劳损伤 …

Creep-rupture behaviour of Nimonic263 alloy coated with 87.5 wt.% Na 2 SO 4+ 5 wt.%
NaCl+ 7.5 wt.% NaVO 3 (3SM) and 74 wt.% Na 2 SO 4+ 21.7 wt.% NaCl+ 4.3 wt.% NaVO 3 …

Hot corrosion fatigue is the key factor affecting the service life of hot section components due
to combined effect of high temperature, mechanical load and salt spray atmosphere for gas …