The hot deformation behavior of fine grained Inconel 718 superalloy was investigated by
compression test in the temperature range of 950 to 1150° C and strain rate range of 0.1–10 …

New high-performance engine concepts for aerospace and automotive application enforce
the development of lightweight intermetallic γ-TiAl based alloys with increased high …

Dynamic softening behavior of TC18 titanium alloy have been investigated in this paper
based on isothermal compression experiment. Strain-rate sensitivity coefficient m and …

The hot deformation behavior of as-cast TC21 titanium alloy has been investigated in the
isothermal compression of the alloy using processing maps conducted at the deformation …

Titanium and its alloys, owing to their properties like high strength, toughness, corrosion
resistance and thermal stability, are employable in various engineering and medical …

Abstract Al-Cu-Li alloy (AA2195) was produced using vacuum induction melting (VIM)
furnace under dynamic argon atmosphere. The as-cast billets were homogenized using a …

Abstract Powder metallurgy (P/M) Ti–22Al–25Nb alloy billets were fabricated by hot pressing
(HP) from argon atomized pre-alloyed powders at a temperature of 1050° C under a …

Workability consists of two independent parts: state-of-stress (SOS) workability and intrinsic
workability. The traditional processing maps proposed by Prasad on the base of dynamic …

Isothermal compression testing of as-cast Ti60 titanium alloy is carried out at the deformation
temperature range of 970–1120° C with 50° C intervals, strain rate range of 0.01–10s− 1 …

The hot deformation behavior of an Al–5.7 wt.% Mg alloy with erbium has been investigated.
Compression tests are performed in the temperature range of 300–500° C and in the strain …