Corrosion of FeCrAl alloys used as fuel cladding in nuclear reactors
The safety of nuclear power plants has put forward new requirements for the corrosion
resistance of fuel cladding with the advancement of industrialization. FeCrAl alloys are …
resistance of fuel cladding with the advancement of industrialization. FeCrAl alloys are …
Crystallographic orientation control of pure chromium via laser powder bed fusion and improved high temperature oxidation resistance
O Gokcekaya, N Hayashi, T Ishimoto, K Ueda… - Additive …, 2020 - Elsevier
This is the first comprehensive study on the development of a cubic crystallographic texture
in pure chromium (Cr) manufactured using laser powder bed fusion (LPBF) with different …
in pure chromium (Cr) manufactured using laser powder bed fusion (LPBF) with different …
Effect of molybdenum addition on oxidation behavior and secondary protection mechanism of FeCrAl coatings
R Zhou, F Wang, K Xu, Y Yuan, L Chen, M Lou… - Materials …, 2023 - Elsevier
FeCrAl alloy coatings are widely used for their excellent oxidation resistance at high
temperatures, but they can suffer from rapid material degradation due to breakaway …
temperatures, but they can suffer from rapid material degradation due to breakaway …
[HTML][HTML] Long-term corrosion behavior of FeCr (Al, Ni) alloys in O2+ H2O with KCl (s) at 600° C: Microstructural evolution after breakaway oxidation
V Ssenteza, J Eklund, S Bigdeli, T Jonsson - Corrosion Science, 2024 - Elsevier
The microstructural evolution of the oxide scales formed on FeCr (Al, Ni) alloys after
breakaway oxidation was studied in 5% O 2+ 20% H 2 O+ N 2 (Bal)+ KCl (s)/KCl (g) at 600° …
breakaway oxidation was studied in 5% O 2+ 20% H 2 O+ N 2 (Bal)+ KCl (s)/KCl (g) at 600° …
Effect of minor addition of Ce on microstructure and LBE corrosion resistance for CLAM steel
W Luo, Q Huang, L Luo, Z Xiao, J Wei, H Cao - Corrosion Science, 2022 - Elsevier
Ce-CLAM specimens were exposed to lead-bismuth eutectic (LBE) for 1500 h under 10− 6
wt% oxygen concentration at 500° C. The continuity and integrity of the oxide scale were …
wt% oxygen concentration at 500° C. The continuity and integrity of the oxide scale were …
[HTML][HTML] High temperature corrosion behavior of FeCrAlSi model alloys in the presence of water vapor and KCl at 600 C–The influence of Cr content
J Eklund, I Hanif, S Bigdeli, T Jonsson - Corrosion Science, 2022 - Elsevier
The corrosion behavior of Fe (5− 20) Cr3Al2Si model alloys and the underlying mechanisms
after breakaway oxidation was investigated at 600° C. Rapid breakaway oxidation was …
after breakaway oxidation was investigated at 600° C. Rapid breakaway oxidation was …
[HTML][HTML] The long-term corrosion behavior of FeCrAl (Si) alloys after breakaway oxidation at 600 C
J Eklund, A Persdotter, V Ssenteza, T Jonsson - Corrosion Science, 2023 - Elsevier
The long-term corrosion behavior of three FeCrAl (Si) alloys has been investigated in two
environments (K 2 CO 3 and KCl+ H 2 O) at 600° C. The FeCrAl alloy experienced …
environments (K 2 CO 3 and KCl+ H 2 O) at 600° C. The FeCrAl alloy experienced …
Oxidation after breakdown of the chromium-rich scale on stainless steels at high temperature: internal oxidation
T Jonsson, S Karlsson, H Hooshyar, M Sattari, J Liske… - Oxidation of metals, 2016 - Springer
Breakaway oxidation of alloy 304L at 600° C was studied in four environments (O 2+ H 2 O+
KCl, O 2+ H 2 O+ SO 2+ KCl, H 2+ H 2 O+ Ar, O 2+ K 2 CO 3) for up to 168 h. The resulting …
KCl, O 2+ H 2 O+ SO 2+ KCl, H 2+ H 2 O+ Ar, O 2+ K 2 CO 3) for up to 168 h. The resulting …
[HTML][HTML] Experimental and thermodynamic investigations on the chlorine-induced corrosion of HVOF thermal sprayed NiAl coatings and 304 stainless steels at 700 C
Alumina-forming β-NiAl coatings were deposited by high velocity oxy-fuel (HVOF) thermal
spraying onto 304 stainless steels for protection against chlorine induced corrosion in a …
spraying onto 304 stainless steels for protection against chlorine induced corrosion in a …
[HTML][HTML] Effects of H2 on microstructures of Cr2O3 scales grown in water vapour and consequences for breakaway
TD Nguyen, J Zhang, DJ Young - Corrosion Science, 2024 - Elsevier
Abstract Model alloy, Fe-20Cr (wt%), was exposed in Ar-(5, 20) H 2 O, Ar-(5, 20) H 2 O-5H 2
and Ar-20O 2 (vol%) at 750 and 850° C. The alloy formed Cr 2 O 3 scales plus Fe-rich oxide …
and Ar-20O 2 (vol%) at 750 and 850° C. The alloy formed Cr 2 O 3 scales plus Fe-rich oxide …