Advances in the nanotechnology have been actively applied to the field of aerospace
engineering where there is a constant necessity of high durable material with low density …

Ceramic matrix composites (CMCs) are designed to overcome the main drawback of
monolithic ceramics, namely their brittleness, and are constituently expressed as a …

The effect of co-doping of titania and manganese oxide at different weight percentages (0.5–
5 wt%) on sintering behaviour and mechanical properties of alumina were evaluated. The …

In this study, ceramic matrix composite specimens constituting Nextel™ 720 fibers and
alumina matrix were subjected to one-sided thermal shock and subsequent 30-min hold at …

Nextel™ 720/alumina based ceramic matrix composite plates were subjected to one-sided
thermal shock and 30-minute hold at 1100° C, 1250° C, 1400° C and 1550° C. Post …

Corrosion on turbine blades in calcium magnesium alumino-silicate (CMAS) environment is
a crucial failure for turbine engines and its components. In this study, oxide-oxide (OO) …

To overcome the inherent brittle nature of ceramics and to optimize their favorable
properties, new design philosophies and novel concepts for manufacturing are needed …

Mullite fiber felt is a promising material that may fulfill the demands of advanced flexible
external thermal insulation blankets. However, research on the fabrication and performance …

The notch effects on the mechanical behavior of Liquid Silicon Infiltration (LSI) based
continuous carbon fiber reinforced silicon carbide (C/C-SiC) was studied. The in-plane (IP) …

ZrSi2 was fabricated via reactive hot-pressing technique for 45 min at 1250° C and 1350° C,
respectively. The hot-pressed sample exhibited Vickers hardness of 10.93±0.32 GPa and …