The effect of molding and gating system design on hydrogen induced crack defects in steel castings
Hydrogen cracking occurs due to the build-up of gas pressure at inclusions, generally
manganese sulfide inclusions. Cracking occurs in the thickest parts of a section, distance to …
manganese sulfide inclusions. Cracking occurs in the thickest parts of a section, distance to …
The effect of metal turbulence on hydrogen induced crack defects in steel castings
In the study, various moulding and gating system designs have been designed for steel
castings in the ÇİMSATAŞ foundry and the effects of the metal turbulence on hydrogen …
castings in the ÇİMSATAŞ foundry and the effects of the metal turbulence on hydrogen …