Powders based on β-tricalcium phosphate (β-TCP) containing sulphate groups at up to 12.0
mol.% were synthesised by chemical precipitation from aqueous solutions. The obtained …

Механохимическим методом синтезированы порошки на основе сульфата кальция с
замещением катионов кальция на катионы магния в количестве 10, 20 и 40 мол …

Calcium sulfate-based powders with magnesium substituting for calcium cations in amounts
of 10, 20, and 40 mol% were synthesized by the mechanochemical method. The phase …

Calcium sulfate-based powders with contents of phosphate groups of 5, 10, and 20 mol%
were synthesized by chemical precipitation from aqueous solutions. The products were …

Materials based on calcium sulfate in which Na+ or K+ cations were substituted to a
concentration of 5, 10, or 20 mol% for Ca 2+ cations were synthesized and studied. The …

Синтезированы и исследованы материалы на основе сульфата кальция, в которых
катионы Са2+ замещали на катионы Na+ или К+ в количестве 5, 10 и 20 мол.%. При …

Работа выполнена при поддержка гранта РФФИ «Создание кальцийфосфатных
композиционных костных цементов, содержащих гранулы сульфата кальция: влияние …

Calcium sulphate-based materials were synthesized and investigated, in which Ca 2+
cations were substituted for Na+ or K+ cations in an amount of 5, 10 and 20 mol.%. With the …

New materials based on calcium sulphate with the replacement of calcium cations to
magnesium cations–10, 20 and 40 mol.% were obtained. The synthesis of substituted forms …