A review on failure mechanism of thermal barrier coatings and strategies to extend their lifetime
G Mehboob, MJ Liu, T Xu, S Hussain, G Mehboob… - Ceramics …, 2020 - Elsevier
Thermal barrier coating (TBC) system is an essential technology in many fields associated to
high temperatures. The main function of these TBCs is to protect the metallic parts against …
high temperatures. The main function of these TBCs is to protect the metallic parts against …
An influence of oxygen flow rate and spray distance on the porosity of HVOF coating and its effects on corrosion—A review
Thermal spray coating, exceptionally high-velocity oxyfuel (HVOF), improves the corrosion
resistance and wear of metal. Coating parameters play a vital role in the properties of the …
resistance and wear of metal. Coating parameters play a vital role in the properties of the …
Oxidation and hot corrosion resistance of HVOF/EB-PVD thermal barrier coating system
Hot corrosion and oxidation cause very destructive damage in thermal barrier coatings
(TBCs) during service conditions. In hot corrosion, TBCs exposed to molten salts lose their …
(TBCs) during service conditions. In hot corrosion, TBCs exposed to molten salts lose their …
Preparation of Gd2Zr2O7 nanoceramics by flash sintering and two-step flash sintering
J Yang, M Fu, Q Tian, L Meng, L Zhang, Y Liu, J Xie… - Ceramics …, 2023 - Elsevier
Abstract Preparation of Gd 2 Zr 2 O 7 nanoceramics using a simple and low energy-
consuming approach is significant for their wide range of applications. In this work, flash …
consuming approach is significant for their wide range of applications. In this work, flash …
Hot corrosion behavior of dense CYSZ/YSZ bilayer coatings deposited by atmospheric plasma spray in Na2SO4+ V2O5 molten salts
J De la Roche, JM Alvarado-Orozco, PA Gomez… - Surface and Coatings …, 2022 - Elsevier
In this work, the hot corrosion (HC) resistance of bilayer thermal barrier coatings (TBC)
architectures composed of dense Ceria-Yttria Stabilized Zirconia (CYSZ) and Yttria …
architectures composed of dense Ceria-Yttria Stabilized Zirconia (CYSZ) and Yttria …
Efficacious elimination of crystal violet pollutant via photo-Fenton process based on Gd(2−x)La(x)Zr2O7 nanoparticles
The photo-Fenton process is an appropriate method of the Advanced Oxidation Process that
is used in the photocatalysis of organic dyes like crystal violet (CV). La3+ ion substituted …
is used in the photocatalysis of organic dyes like crystal violet (CV). La3+ ion substituted …
Phase evolution and hot corrosion behavior of Yb2O3 and CeO2 co-doping YSZ ceramics under high temperature
D Liu, Y Jing, X Cui, Z Chen, X Wang, Y Fang, A Liu… - Ceramics …, 2023 - Elsevier
The phase instability of 6–8 wt% Y 2 O 3 partially stabilized ZrO 2 (YSZ) in high temperature
and molten salt corrosion environment seriously limits its application above 1200° C. In this …
and molten salt corrosion environment seriously limits its application above 1200° C. In this …
Improving the thermal shock resistance and fracture toughness of synthesized La2Ce2O7 thermal barrier coatings through formation of La2Ce2O7/YSZ composite …
AMF Dehkharghani, MR Rahimipour… - Surface and coatings …, 2020 - Elsevier
Due to the substantial brittleness of the thermal sprayed coatings, fracture mechanic can
effectively illustrate the applicability of such surface layers. Lanthanum-cerium oxide (LC) …
effectively illustrate the applicability of such surface layers. Lanthanum-cerium oxide (LC) …
A2Zr2O7 (A= La/Gd/Yb): Grain growth effect on phase stability properties at 1300° C
The present study aims to investigate the influence of grain growth during heat treatment on
the phase stability of AZO: A 2 Zr 2 O 7 compounds at 1300° C. To this end, three cations of …
the phase stability of AZO: A 2 Zr 2 O 7 compounds at 1300° C. To this end, three cations of …
Corrosion behavior of high-entropy (La0. 2Nd0. 2Sm0. 2Eu0. 2Gd0. 2) Ce2O7 in different aggressive molten salt
Y Xue, X Zhao, Y An, H Nie, M Gao, H Zhou, J Chen - Corrosion Science, 2022 - Elsevier
Abstract High-entropy (La 0.2 Nd 0.2 Sm 0.2 Eu 0.2 Gd 0.2) Ce 2 O 7 (HECO) was
synthesized as a potential thermal barrier material. The hot corrosion behavior of HECO in …
synthesized as a potential thermal barrier material. The hot corrosion behavior of HECO in …