Chitosan fibers showing narrow diameter distribution with a mean of 42 nm were produced
by electrospinning and utilized for the sorption of Fe (III), Cu (II), Ag (I), and Cd (II) ions from …

The metal adsorbability of the chitosan electrospun nanofiber (∼ 235nm in diameter) mats
was examined in an aqueous solution. The chitosan nanofiber mats (which were neutralized …

The chitosan/TiO 2 composite nanofibrous adsorbents were developed by two techniques
including TiO 2 nanoparticles coated chitosan nanofibers (coating method) and …

In this study, chitosan/poly (ethylene oxide) nanofibres were fabricated at different chitosan:
PEO weight ratio by electrospinning process. The effects of chitosan/PEO composition onto …

Uniform chitosan composite nanofiber mats (CS/PAAS) containing 4.0 wt% polyacrylic acid
sodium loading have been prepared by electrospinning, followed by annealing at elevated …

Stacked chitosan nanofibers with an average diameter of 75 nm were successfully produced
by electrospinning using 5 wt% chitosan in acetic acid as the spinning solution. The fibers …

Abstract Chitosan/cellulose (CS/CL) nanofibers were fabricated through electrospinning with
a mixture of chitosan (CS) and cellulose acetate (CA) in a co-solvent system …

Low-cost and biocompatible chitin nanofiber and chitosan nanoparticle as natural polymers
synthesized successfully by means of a mechanical and a chemical procedure respectively …

Contamination of water resources by toxic heavy metals has significant impacts on
environmental and human health. Their removal from aqueous media is essential to ensure …

A novel step wise synthetic route was developed to prepare amine grafted nanofibers
(AGNFs) affinity membrane. The chemical structure of the nanofibers (NFs) after grafting was …