Structure, castability and mechanical properties of commercially pure and alloyed titanium cast in graphite mould

WW Cheng, CP JU, JHC Lin - Journal of Oral Rehabilitation, 2007 - Wiley Online Library
WW Cheng, CP JU, JHC Lin
Journal of Oral Rehabilitation, 2007Wiley Online Library
summary This report is a study of structure, castability, mechanical properties as well as
corrosion behaviour of titanium doped with up to 5 weight percentage (wt%) of a series of
alloy elements, including Ta, Mo, Nb, Hf, Zr, Sn, Bi and Ag. The results indicate that, with
addition of 1 wt% alloy element, Bi and Mo were most effective in enhancing the castability
of titanium. With more alloy elements added, the castability values of most alloys more or
less decreased. Except Ti–Mo system, all Ti alloys with a fine acicular morphology had the …
Summary
 This report is a study of structure, castability, mechanical properties as well as corrosion behaviour of titanium doped with up to 5 weight percentage (wt%) of a series of alloy elements, including Ta, Mo, Nb, Hf, Zr, Sn, Bi and Ag. The results indicate that, with addition of 1 wt% alloy element, Bi and Mo were most effective in enhancing the castability of titanium. With more alloy elements added, the castability values of most alloys more or less decreased. Except Ti–Mo system, all Ti alloys with a fine acicular morphology had the same crystal structure (hcp) as that of c.p. Ti with a typical lath type morphology. When 3 wt% or more Mo was added, a finer orthorhombic α’’ phase was formed. The microhardness and bending strength values of Ti alloys were all higher than those of c.p. Ti. Among all alloys, Ti–Mo system exhibited the highest hardness and strength level. For a certain alloy, the bending strength did not necessarily increase with its alloy content. Except Ti‐5Zr and Ti–Mo alloys, the bending moduli of most alloy systems were not much different from that of c.p. Ti. All alloys showed an excellent resistance to corrosion in Hanks’ solution at 37 °C.